Composite film

ABSTRACT

The invention relates to a composite film (1), preferably intended for use in the construction industry and/or preferably for use as a construction film, having at least one functional layer (2), at least one outer protective layer (3) and at least one inner protective layer (4), the functional layer (2) being arranged between the outer protective layer (3) and the inner protective layer (4). According to the invention, it is provided that the functional layer (2) is formed as at least a single-layer membrane layer, that the outer protective layer (3) and the inner protective layer (4) are formed as a nonwoven layer comprising a polyolefin, and that the outer protective layer (3) and/or the inner protective layer (4) comprises at least one bicomponent fiber (5) having a first component (6) and a second component (7), the first component (6) comprising a first polymer and the second component (7) comprising a second polymer as constituent.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a national stage application under 35 U.S.C. 371 ofPCT Application No. PCT/EP2019/075797 having an international filingdate of 25 Sep. 2019, which designated the United States, which PCTapplication claimed the benefit of German Application No. 10 2018 008583.0, filed 31 Oct. 2018, each of which are incorporated herein byreference in their entirety.

The invention relates to a composite film, preferably intended for usein the construction industry and/or preferably for use as a constructionsheet. The composite film has at least one functional layer. Inaddition, the composite film has at least one outer protective layer andat least one inner protective layer. The functional layer is arrangedbetween the outer protective layer and the inner protective layer.

Composite films used in the construction industry are used to protectbuildings, building materials and/or for cover, in particular ofbuildings. In particular, composite films can be used as facademembranes, construction films and/or roof membranes.

According to the invention, however, the composite film can also be usedin other areas, for example in agriculture, as a geotextile and/or inthe packaging industry.

Ultimately, the composite film can serve to preserve the value of goods,in particular buildings and/or building materials. For example, thecomposite film can be used to protect against the elements, inparticular to protect against rain, snow, moisture, cold, heat and/orwind. Consequently, the composite film may also be referred to as aprotective film.

Various composite films are known from practice that have a multilayerstructure and/or a structure consisting of several layers. However,these films have a number of disadvantages. For example, the multilayercomposite films known in practice do not succeed in providing themechanical properties required for the respective application at a highwater vapor permeability—i.e. at an Sd value of less than 0.1 m—whileensuring a good bond between the individual layers.

The functional layer, which is known in practice, ensures watertightness, water vapor permeability and/or wind tightness for thecomposite film. The protective layers on the outside serve to protectthe functional layer, especially in the event of mechanical stress.However, this protection cannot usually be ensured for a longer period,in particular for more than 10 years, while maintaining a highmechanical stability of the protective layers. In addition, protectivelayers that bond well with other layers of the composite film areassociated with high manufacturing costs.

It is now the object of the present invention to avoid theaforementioned disadvantages of the prior art.

According to the invention, the aforementioned object is solved in acomposite film of the type mentioned above in that the functional layeris formed as at least a single-layer membrane layer, in that the outerprotective layer and the inner protective layer are formed as a nonwovenlayer comprising polyolefin, and in that the outer protective layerand/or the inner protective layer comprises at least one bicomponentfiber having a first component and a second component, the firstcomponent comprising a first polymer and the second component comprisinga second polymer as a constituent.

The outer protective layer can be understood as the protective layerfacing the weather side—provided that the composite film is used forprotection against the weather. In principle, it is also conceivablethat the composite film is not used for weather protection. In thiscase, the arrangement of the outer protective layer and the innerprotective layer would be interchangeable. In particular, however, theinner protective layer faces the goods to be protected, for example theinterior of the building, the building material or the like.

According to the invention, the composite film exhibits very goodweathering stability—with simultaneous high UV stability. Thus, thecomposite film can be used for a longer period of time, while ensuringat least substantially the required weathering properties over thisperiod. In particular, the composite film has a service life of longerthan 10 years, preferably between 15 and 60 years.

By using the bicomponent fiber in at least one protective layer, theoverall strength of the composite film can be significantly increased,preferably by at least 10%, more preferably between 20% to 70%.

The protective layer comprising the bicomponent fiber is advantageouscompared with nonwoven layers known from the prior art, in particularpolypropylene or polyethylene nonwoven layers, in that it ensuresincreased mechanical strength. In addition, the protective layercomprising the bicomponent fiber can be hydrophobic (water-repellent).Improved strength is shown to be particularly advantageous in the caseof longer-term and/or increased mechanical stress on the composite film.If, for example, the composite film is used as a roofing sheet, inparticular underlayment and/or sarking membrane, it is exposed tomechanical stresses not only during installation but also when the roofis walked on, for example by roofers.

In a particularly preferred embodiment, the functional layer is designedas a monolithic membrane layer. A monolithic membrane layer isunderstood to mean in particular a closed-cell and/or pore-free layer ofa membrane. Monolithic membrane layers can in particular ensureparticularly good protection against driving rain while at the same timebeing open to diffusion. Unlike the conventional microporous membranelayer, moisture transport can take place actively along the molecularchains by diffusion.

Furthermore, a membrane layer is understood to be a layer of this typethat exhibits selective permeability. Membranes can be of differenttypes and, in particular, can take the form of films or textiles.Membrane layers ensure, for example, when used as or in a subroofmembrane, that the external influences of the weather do not have adamaging effect on the interior of the building.

Preferably, the functional layer has plastic and/or synthetic resin asmaterial and/or consists thereof. Furthermore, in particular anelastomeric and/or a thermoplastic material is provided as material forthe functional layer, preferably polyurethane plastic, in particularthermoplastic polyurethane (TPU). Preferably, the functional layer ismade of thermoplastic polyurethane. A TPU film exhibits high mechanicalstability and is in particular at least substantially resistant toweathering and/or environmental influences.

In addition, the functional layer can have a grammage and/or basisweight of less than 100 g/m². In particular, the grammage is between 1g/m² to 70 g/m², and more preferably between 3 g/m² to 40 g/m².Particularly preferably, the grammage of the functional layer is between4 g/m² to 30 g/m², and more preferably between 5 g/m² to 25 g/m².

In a further particularly preferred embodiment of the invention, it isprovided that the functional layer has at least two layers of membranelayers. On the one hand, these membrane layer layers can be formeddifferently. In addition, on the other hand, at least two membrane layerlayers can be formed at least substantially identically. In particular,in the case of a three-layer structure of the functional layer, it canbe provided that the outer layers enclosing a central layer are at leastsubstantially identically formed. By identical formation is to beunderstood in particular that the membrane layers have the same surfaceproperties and/or the same material and/or the same materialcomposition. Finally, the identical membrane layers may have the samefunctional design. For example, however, the grammage of the identicallyformed membrane layers may differ from one another by less than 5 g/m².

Preferably, the membrane layers may have the same or a differentproportion of additives, in particular with respect to the relativeadditive amount and/or the type or material of the additive(s). Inparticular, at least two membrane layer layers, preferably the outermembrane layer layers, may have the at least substantially same oridentical material, preferably TPU, with a different additive addition.The additive addition can be shown or reflected in a different amount ormass of the additive—relative to the volume and/or the area of themembrane layer and/or the total amount—and/or in a different additivecomposition.

It is particularly preferred that at least one membrane layer of thefunctional layer, in particular an outer membrane layer preferablyfacing the outer protective layer and/or the inner protective layer,comprises as material thermoplastic copolyester (TPEE) and/orthermoplastic polyurethane (TPU) and/or consists thereof. Furthermore,in a preferred embodiment of the invention, the functional layer may beformed from TPEE layers and/or TPU layers and/or from TPEE layers aswell as TPU layers. In particular, the TPEE layers and/or the TPU layersand/or the membrane layers of the functional layer are firmly bonded toone another, in particular inseparably. TPEE layers have a good and/orhigh tear propagation resistance with a high strength as well asstiffness while ensuring resistance to liquids. A monolithic TPEEmembrane is particularly well extrudable and also suitable for thinfilms. In addition, a TPEE membrane can enable extrusion lamination withPP nonwovens. In particular, a membrane film comprising TPEE is suitablefor a multilayer coextruded film, especially a coextruded compositefilm, and makes sense from a technical point of view.

Thermoplastic polyurethane is particularly intrinsically flame retardantand exhibits good long-term aging behavior, preferably for service livesgreater than 10 years.

In a further preferred embodiment, it is provided that the material ofthe functional layer, in particular the thermoplastic polyurethane, hasa proportion of at least 10%, preferably from 15% to 100%, morepreferably from 20% to 70%, of material originating from renewable rawmaterials. Renewable raw materials are to be understood in particular asorganic raw materials that originate from agricultural and forestryproduction and are used by humans specifically for further applicationpurposes outside the food and feed sector.

In a further preferred embodiment, it is provided that at least oneouter membrane layer layer and/or one inner membrane layer layer of themultilayer functional layer comprises and/or consists of a foamedpolymer. During the extrusion lamination process, the outerside foamedlayer of the functional layer can achieve an interlocking with the outerprotective layers—that is, the outer and/or the inner protectivelayer—as a result of which the composite adhesion with the protectivelayers, in particular the protective layers formed as non-wovenpolypropylene layers, is improved. Preferably, the outer membrane layerof the functional layer comprising the foamed polymer is thus bonded tothe outer and/or inner protective layer, at least also by interlocking.The interlocking can be caused by slower cooling due to the foamedpolymer layer. Kneading swirls in the pressing plant—which are causedduring production, especially during calendering, of the compositefilm—can also contribute to the interlocking. In particular, the foamedpolymer layer penetrates into open pores on the outer side of theprotective layer facing the foamed polymer layer, thus enabling a firmbond to the protective layers.

An inner membrane layer comprising a foamed polymer may be provided toensure nail tightness.

In particular, the outer protective layer and/or the inner protectivelayer can be in the form of a nonwoven layer, preferably thermobonded orneedle-jet or wet-jet bonded. The nonwoven layer may be a polyolefinicnonwoven, in particular a nonwoven layer comprising polypropylene and/orconsisting thereof is provided. Very particularly preferred is theformation of the outer protective layer and/or the inner protectivelayer as a polypropylene needle punched nonwoven layer. The nonwovenlayer ensures in particular the mechanical properties of the compositefilm and also guarantees protection of the functional layer enclosedbetween the protective layers.

Particularly preferably, the outer protective layer and/or the innerprotective layer is formed as a spunbonded layer. A spunbonded nonwovenfabric and/or a spunbonded nonwoven layer has a nonwoven fabric made offibers with at least essentially unlimited length—that is, with longfibers.

Preferably, the fibers of the spunbonded layer provided in the outerand/or inner protective layer are bicomponent fibers. Thus, thespunbonded layer made of continuous fibers can be made of bicomponentcontinuous fibers.

Moreover, in another preferred embodiment of the invention, the basisweight and/or grammage of the outer protective layer and/or the innerprotective layer may be less than or equal to 250 g/m². Preferably, theaforementioned grammage is between 1 g/m² to 250 g/m², furtherpreferably between 10 g/m² and 150 g/m², preferably between 20 g/m² to120 g/m² and in particular between 30 g/m² and 100 g/m². The grammage ofthe protective layers is selected in such a way that the requiredproperties of the composite film, in particular elasticity, stability,tear resistance and/or tear propagation resistance, can still beadequately ensured with the lowest possible total grammage of thecomposite film, wherein the composite film providing mechanicalprotection of the functional layer on account of the protective layerson the outside, which can likewise be referred to as carrier layers.

The inner and outer protective layers may have a different grammageand/or a different basis weight, material composition and/or bicomponentfibers that differ from one another. Alternatively or additionally, itcan be provided that the inner and the outer protective layer are atleast substantially identical and/or identically formed.

An identical design of the protective layers is to be understood inparticular as meaning that the protective layers have the same surfaceproperties, the same material and/or material composition and/or thesame grammage. In particular, the outer and inner protective layers canhave the same function, in particular wherein the grammage of theidentical protective layers differs by less than 5 g/m².

Preferably, a symmetrical structure of the layers of the composite filmis provided.

Furthermore, the outer protective layer and/or the inner protectivelayer can be designed as a mechanically, chemically and/or thermally,preferably thermally, bonded nonwoven layer. A nonwoven layer ischaracterized in particular by low manufacturing costs and highmechanical resistance to external influences.

Preferably, the functional layer is firmly bonded to the outerprotective layer and/or the inner protective layer. In particular, theouter protective layer and/or the inner protective layer may be bondedto the functional layer. Consequently, an adhesive layer may be providedbetween the functional layer and at least one protective layer. Thebonding of the layers may be performed during the manufacturing process,in particular during the extrusion laminating process.

In a further preferred embodiment, the outer protective layer and/or theinner protective layer, in particular the outer protective layer and/orinner protective layer comprising the at least one bicomponent fiber,and/or the functional layer has an adhesion-promoting layer. Theadhesion-promoting layer can in particular be arranged on the outside ofthe outer protective layer, the inner protective layer and/or thefunctional layer.

In particular, the adhesion-promoting layer can be designed as anadhesive layer and/or the adhesion promoter as an adhesive. Preferably,the adhesion-promoting layer and/or the adhesive layer enables amaterial bond between the layers to be joined.

Preferably, an adhesive layer is provided between the membrane layer andthe outer and/or the inner protective layer, in particular over theentire surface, preferably for firm as well as material bonding.

The adhesion-promoting layer may further comprise a polymer, inparticular an adhesion promoter polymer. The adhesion-promoting layermay be firmly bonded to the functional layer, the inner protective layerand/or the outer protective layer. Furthermore, the adhesion-promotinglayer and/or the adhesion promoter polymer may comprise a plastic and/ora synthetic resin, preferably polyurethane.

Furthermore, the adhesion-promoting layer can also be integrated in theinner protective layer, in the outer protective layer and/or in thefunctional layer—in such a way that the adhesion promoter polymer isenclosed and/or arranged in the, in particular outer, surface region ofthe aforementioned layers. Thus, the adhesion-promoting layer can beformed as part or component of the functional layer and/or the outerprotective layer and/or the inner protective layer. Theadhesion-promoting layer can enable a firm connection of the functionallayer to the outer protective layers. The adhesion promoter and/oradhesion promoter polymer enables the protective layers, which areformed as non-woven layers, to be permanently bonded to the functionallayer.

By incorporating functional materials, for example the adhesion promoterpolymer and/or a flame retardant, into the inner and/or outer protectivelayer formed as a nonwoven layer, a cost-effective structure of thecomposite film can be made possible.

By using the adhesion promoter and/or the adhesion promoter polymerand/or the adhesion-promoting layer in the outer layer of the innerand/or outer protective layer, in particular in the inner and/or outerprotective layer comprising the bicomponent fiber, the use of hotmeltscan be dispensed with (hotmelt-free bonding). Thus, the adhesionpromoter and/or the adhesive can already ensure sufficient bondingand/or adhesion to the functional layer.

In addition, the sub-roofing sheet can be designed to be open todiffusion, windproof and/or rainproof, in particular waterproof, and/orwater-repellent and/or permeable to water vapor. The rainproofnessand/or water vapor permeability can be ensured in particular by thediffusion-open functional layer, the functional layer being designed insuch a way that the composite sheet is designed to be water vaporpermeable and/or diffusion-open and/or waterproof, in particular watervapor permeable and waterproof, as a whole.

In the case of a rainproof and/or waterproof design of the compositefilm, it is provided that it withstands a water column of greater than800 mm, preferably between 1,000 mm and 20,000 mm, more preferablybetween 1,500 mm and 9,000 mm. The water column is a unit of measurementthat indicates the waterproofness of technical fabrics. It can bedetermined according to DIN EN 20811:1992, also known as ISO 811 (as ofSeptember 2018).

Preferably, the composite film has an Sd value of less than or equal to0.5 m, preferably from 0.008 m to 0.5 m, more preferably from 0.009 m to0.2 m, more preferably from 0.01 m to 0.1 m. The Sd value indicates thewater vapor diffusion equivalent air layer thickness and is a buildingphysics measure of the water vapor diffusion resistance of a componentor component layer. The vapor permeability of a building material can beassessed via the Sd value. The water vapor diffusion resistance isgraphically described by the thickness of a layer of air that isnecessary so that the same diffusion current—as the component underconsideration—flows through the air layer in a stationary state underthe same conditions. In particular, the composite film is designed to beopen to diffusion, wherein the openness to diffusion is characterized byan Sd value of less than or equal to 0.5 m.

In addition, the tear strength of the composite film can be designed tobe greater than 50 N/mm. Preferably, the tear strength of the compositefilm is between 50 N/mm to 600 N/mm, more preferably between 100 N/mm to400 N/mm. The tear strength of the composite film may correspond to theforce required until crack formation and/or crack expansion. Inparticular, the tear strength is measured according to the ASTMInternational technical standard; namely ASTM D1004 (as of September2018) and ASTM D1925 (as of September 2018).

Preferably, the tear strength of the composite film is greater than 50N/mm. Preferably, the tear strength is between 50 N/mm and 500 N/mm,more preferably between 100 N/mm and 300 N/mm. The tear propagationstrength is a physical parameter that characterizes a material propertyas well as the application range of the composite film. The tearpropagation strength can also be referred to as notch strength. The tearpropagation strength indicates the resistance of a material—in this casethe composite film—not to tear further after being cut or scored. Thehigher the determined value of the tear resistance, the more resistantthe tested material is to further tearing. In contrast, the lower thevalue, the lower the tear resistance of the material. Consequently, thetear propagation strength follows metrologically the measurement of thetear strength.

Both the tear strength and the tear propagation strength can be designedto be direction-dependent, in particular as a function of the fiberdirection (machine direction and transverse direction). Theabove-mentioned tear strengths apply in particular to the machinedirection and/or transverse direction.

The machine direction is the direction in which the nonwoven wastransported in and/or through the machine during production, i.e.regularly the length direction of a nonwoven web. The transversedirection in which the web expands over its surface is the direction atright angles to the machine direction, i.e. regularly the direction inthe width of a web.

Furthermore, according to a further embodiment, it is provided that atleast one reinforcing layer is arranged between the functional layer andthe outer protective layer and/or the inner protective layer. Inparticular, a reinforcing layer can be arranged in each case between theouter protective layer and the functional layer and between the innerprotective layer and the functional layer. The reinforcing layer may beformed as a leno fabric. The reinforcing layer serves in particular toincrease the mechanical stability of the composite film.

Preferably, the reinforcing layer comprises and/or consists of a plasticand/or a synthetic resin, preferably a plastic polymer, in particularpolypropylene and/or polyethylene terephthalate (PET).

Leno fabrics are transparent and/or air-permeable fabrics characterizedby special warp threads. The warp threads form the so-called leno units,in which a ground thread and a loop thread from the warp twist together.In this process, the inclusion of the weft and the twisting of the twowarp threads alternate with each other. In the case of a so-called fulltwist, a complete twist of the warp threads is caused between the weftthreads; in the case of a half twist, a simple interlacing occurs. Inparticular, the fabric has a low grammage. By tightly enclosing the weftthreads from the two warp threads, a sliding strength can be ensured.

In a further preferred embodiment, at least one longitudinal edge-sideadhesive zone is provided on the topside and/or the underside of thecomposite film, in particular on the topside and/or the underside of theouter and/or the inner protective layer. The longitudinal edge-sideadhesive zone is used for bonding adjacent composite films to produce acontinuous film layer consisting of individual composite film strips. Inparticular, the longitudinal edge-side adhesive zone is spaced from thelongitudinal edge of the composite film. Furthermore, the adhesive zonecan be in the form of strips, possibly as interrupted strips.

In particular, the adhesive zone has a width of between 2 to 10 cm.

Further preferably, an adhesive-free area on the surface of the topsideand/or the underside of the composite film of greater than 50%,preferably between 50% to 95%, more preferably between 80% to 90%, isprovided. An adhesive-free or adhesive-free area indicates that portionof the surface of the composite film which is not covered by an adhesivezone. Ultimately, therefore, the adhesive zone is provided along thelongitudinal edge on the topside and/or underside.

It is understood that the composite film may have one adhesive zone, twoadhesive zones and/or a plurality of adhesive zones, for example fouradhesive zones. It may be provided that at least one longitudinaledge-side adhesive zone is provided on the topside and/or the underside.

Thus, at least one—in particular exactly one—adhesive zone can beprovided on both the topside and the underside. Furthermore, twoedge-side adhesive zones can also be provided on the top or underside.In a further embodiment, one adhesive zone is provided in the region ofeach of the four longitudinal edges of the composite sheet, so that thecomposite sheet has four adhesive zones.

Preferably, the adhesive zones are between 1 to 90 mm from thelongitudinal edge, preferably between 3 to 70 mm, more preferablybetween 5 to 50 mm.

In addition, a strip-shaped design of the adhesive zones can enable aclean and simple arrangement of the sheets one above the other, inparticular in the case of an adhesive-in-adhesive bond. In the case of astrip-shaped formation of the adhesive zones, it is provided that inparticular the number of strips is between 1 to 15, preferably between 3to 12, more preferably between 5 to 9. The strip width of a strip of theadhesive zone can in particular be between 1 to 30 mm, preferablybetween 1.5 to 10 mm, more preferably between 2 to 5 mm.

Preferably, the bonding of the adhesive zones is carried out in such away that, when an adjacent composite film is bonded, a windproof and/orairtight bond is formed between the two composite films. In particular,as a result, no wind can penetrate between the bonded areas. Inparticular, an adhesive-in-adhesive bond is effected, that is to say theadhesive zones are arranged one above the other, at least in certainareas, in such a way that a firm and permanent bonding of the rows ofcomposite films is effected. In this context, it is understood that theadhesive zones can be of the same design and/or can have properties thatdiffer from one another.

In addition, the offset of the top and underside adhesive zones from alongitudinal edge of the composite sheet may be provided such that whenadjacent sheets are bonded, there is only a partial adhesive-in-adhesivebond between the adhesive zones of adjacent composite sheets or even nosuch bond. As previously explained, the adhesive-in-adhesive bondenables windproof, airtight, diffusion-open and/or waterproof bonding ofthe composite film. Thus, the required properties of the composite filmcan also be adequately ensured at the transition areas of the compositefilm, in particular the longitudinal edge area, preferably wheninstalled on a pitched roof.

In a further preferred embodiment of the invention, it is provided thatthe mating surface for the adhesive zone comprising the adhesive iscovered and/or surface-treated with a liner, in particular in the formof a peel-off strip. By covering the adhesive and/or the adhesive zones,it can be ensured that there is no contamination of the adhesive zonewhen the composite film is laid, and/or that the degree of contaminationis kept as low as possible. Consequently, a windproof and/or watertightbond can be produced, preferably via an adhesive-in-adhesive bond.

According to the invention, it is provided that the inner protectivelayer and/or the outer protective layer comprises at least onebicomponent fiber and/or has a bicomponent fiber structure. Inparticular, the inner and/or outer protective layer formed as a nonwovenlayer is formed as a nonwoven layer of bicomponent fibers. Inparticular, a bicomponent fiber spunbond layer is provided.

Bicomponent fibers of the type in question usually have a firstcomponent made of a first polymer and a second component made of asecond polymer. A distinction can be made between different types ofbicomponent fibers, each having different characteristic distributionsof the components in the fiber cross-section. Bicomponent fibers inwhich the first component surrounds and thus encloses the secondcomponent in the cross-section of the fiber are referred to ascore-sheath fibers. Bicomponent fibers in which both the first componentand the second component form part of the fiber surface in thecross-section of the fiber are referred to as side-by-side fibers.Fibers with structures in which multiple strands of one component areembedded in a strand of the other component, resulting in an imageresembling a plurality of islands formed from one component incross-section, are referred to as island-in-the-sea fibers. Bicomponentfibers in which a plurality of regions of each component are present incross-section and form the outer fiber surface are referred to assegmented-pie fibers, since the regions of the individual componentsregularly have a pie-piece-like division in cross-section. Bicomponentfibers within the meaning of the present application are also expresslyunderstood to be those fibers which have more than two components.

The purpose of bicomponent fibers is to improve the properties of thefibers or the properties of the spunbonded nonwovens produced from thefibers. The properties of a spunbonded nonwoven depend on a large numberof influencing factors. Some of these factors influencing the propertiesof a spunbonded nonwoven are properties of the fibers used, such astheir strength. A widely accepted theory, at least in its basic concept,is that the properties of the resulting bicomponent fiber then representa combination of the properties of the individual components of thebicomponent fiber, in which the properties of the individual componentscomplement each other as far as possible so that the advantages of theproperties of both components are combined in the bicomponent fiber. If,for example, a fiber is desired that both exhibits high strength andalso exhibits advantageous behavior when the fibers are bonded to oneanother during nonwoven production, it is a good idea to combine a firstcomponent that exhibits high strength with a second component thatexhibits good bondability.

Additives are often added to the polymers to improve the properties ofthe bicomponent fibers. The additives can be a wide variety ofsubstances. They can be used, for example, for coloring,thermostabilization, flame retardancy, hydrophilization orhydrophobization, or UV stabilization. The additives are regularlydistributed evenly in the phase.

The first polymer and the second polymer may be formed at leastsubstantially identically, in particular wherein the first component andthe second component have additives and/or additive compositions and/oradditive amounts that differ from one another.

Preferably, the first component has an additive, the mass fraction ofthe additive in the second component being smaller than in the firstcomponent. According to the invention, the first component can thus havean additive for influencing and/or improving properties.

Preferably, the mass fraction of the additive of the first component inthe second component is at most 66.6%, further preferably at most 50%and in particular at most 33.3%. Very preferably, the additive is notpresent in the second component.

Preferably, the mass fraction of the first component in the bicomponentfiber is at most 50%, preferably 25%, particularly preferably 10%, veryparticularly preferably 5%. The bicomponent fiber is particularlypreferably a core-sheath fiber, with the first component forming thesheath.

The advantage of concentrating the additives in the first componentsurrounding the second component is that it has been shown that theamount of additive required in the second component can be lower thanwith the usual equal distribution of the additive in the two components,if the same or an improved effect of the additive is to be produced.

Additive in this sense means additives which are added to the polymer inthe respective component in order to modify and thereby improve theproperties of the resulting fiber or the spunbonded web obtained fromthe fiber.

For example, when performing a fire test according to EN 13501-1, it canbe seen that with the distribution of the additive in the componentsaccording to the invention, a smaller amount of the additive in total,in this example a flame retardant, is sufficient to lead to a positivetest result than if the flame retardant is evenly distributed in thefiber. In this test, the entire fiber is covered by the flame withinfractions of a second, so the beneficial effect cannot be readilyattributed to some sort of shielding effect of the sheathing area of thefiber.

The additives, which are added to the polymers in low concentrations,basically represent an impurity of the polymer with regard to fiberproduction. In the case of impurities, there is basically always therisk that the behavior of the components will change during themanufacture of the fiber due to these impurities. Therefore, from thepoint of view of the skilled person, an uneven distribution of theadditives in the components of the bicomponent fiber initially involvesthe risk that the quality of the bicomponent fiber or the stability ofthe manufacturing process will deteriorate. Moreover, from the point ofview of the skilled person, it is regularly not important that anadditive is concentrated in a particular zone of the fiber. This is dueto the low thickness of the fibers in question. Similar to the situationwith dyes or pigments, it also makes no obvious sense from the point ofview of the skilled person to concentrate additives in a specific zoneof the fiber. For example, in the case of a flame retardant, the entirefiber will be affected by the combustion processes anyway. Also, UVradiation will penetrate the entire fiber. Nevertheless, it has beenshown surprisingly that in some cases even particularly advantageousresults can be obtained if the additive in the one component is not onlyreduced but omitted altogether. In any case, one advantage ofconcentrating the additives in the first component is the cost savingdue to the lower additive quantity required.

Advantageously, the additive is a primary or secondary antioxidant, a UVabsorber, a UV stabilizer, a flame retardant, an antistatic agent, alubricant, a metal deactivator, a hydrophilizing agent, a hydrophobizingagent, an antifogging additive and/or a biocide. The following classesof substances and mixtures thereof are particularly preferred:

-   -   Sterically hindered phenols, aromatic secondary or tertiary        amines, aminophenols, aromatic nitro or nitroso compounds as        primary antioxidants.    -   Organic phosphites or phosphonates, thioethers, thioalcohols,        thioesters, sulfides and sulfur-containing organic acids,        dithiocarbamates, thiodipropionates, aminopyrazoles,        metal-containing chelates, mercaptobenzimidazoles as secondary        antioxidants.    -   Hydroxybenzophenones, cinnamates, oxalanilides, salicylates, 1,3        benzenediol monobenzoates, benzotriazoles, triazines,        benzophenones and UV-absorbing pigments such as titanium dioxide        or carbon black as UV absorbers.    -   Metal-containing complexes of organic sulfur or phosphorus        compounds, sterically hindered amines (HALS) as UV stabilizers.    -   Metal hydroxides, borates, organic compounds containing bromine        or chlorine, organic phosphorus compounds, antimony trioxide,        melamine, melamine cyanurate, exfoliated graphite or other        intumescent systems as flame retardants.    -   Quaternary ammonium salts, alkyl sulfonates, alkyl sulfates,        alkyl phosphates, dithiocarbamates, (earth) alkali metal        carboxylates, polyethylene glycols and their esters and ethers,        fatty acid esters, ethoxylates, mono- and diglycerides,        ethanolamines as antistatic agents.    -   Fatty alcohols, esters of fatty alcohols, fatty acids, fatty        acid esters, dicarboxylic acid esters, fatty acid amides, metal        salts of fatty acids, polyolefin waxes, natural or artificial        kerosenes and their derivatives, fluoropolymers and        fluoroligomers, antiblocking agents such as silicas, silicones,        silicates, calcium carbonate, etc. as lubricants.    -   Amides of mono- and dicarboxylic acids and their derivatives,        cyclic amides, hydrazones and bishydrazones, hydrazides,        hydrazines, melamine and its derivatives, benzotriazoles,        aminotriazoles, sterically hindered phenols in combination with        complexing metal compounds, benzylphosphonates, pyridithiols,        thiobisphenol esters as metal deactivators.    -   Polyglycols, ethoxylates, fluoropolymers and fluoroligomers,        montan waxes, especially stearates, as hydrophilizing,        hydrophobizing or anti-fogging agents.    -   10,10′-oxybisphenoxarsine (OBPA),        N-(trihalomethylthiol)phthalimide, tributyltin oxide, zinc        dimethyldithiocarbamate, diphenylantimony-2-ethylhexanoate,        copper-8-hydroxyquinoline, isothiazolones, silver and silver        salts as biocides.

Advantageously, the difference between the melting points of the firstcomponent and the second component is less than or equal to 8° C. Itshould be noted that any individual intervals or individual values areincluded in the specified intervals and are to be regarded as disclosedas essential to the invention, even if they are not mentioned in detail.

In connection with the advantageous choice of melting points, it hasbeen surprisingly shown that in the case of bicomponent fibers, wherethe two components have similar melting points, an improvement in thesynergistic effects between the properties of the two components can beachieved. This relates in particular to mechanical properties. Forexample, in the case of a spunbonded nonwoven made from bicomponentfibers according to the invention, it is possible to increase both thespecific tear strength and the specific nail pull-out force. In the caseof conventional prior art fibers, measures taken in the manufacture ofspunbonded nonwovens from these fibers to increase the specific tensilestrength were regularly accompanied by a reduction in the specific nailpull-out force. Conversely, measures to increase the specific nailpull-out forces regularly led to a decrease in the specific tear-outforces. These disadvantageous effects can be avoided or at leastmitigated with the advantageous bicomponent fibers.

Among the positive effects of the present invention is that the amountof recycled material that can be added to one of the components in themanufacture of the bicomponent fiber is increased compared toconventional fibers. It has been shown that when components with meltingpoints combined according to the invention are used, the change in theproperties of a component caused by the addition of recycled material ismuch less than with conventional fibers.

Preferably, the component with the lower melting point forms the outersurface of the fiber in the cross-section of the fiber. Preferably, thecomponent with the lower melting point surrounds the component with thehigher melting point. This advantageous embodiment results in the lowermelting point component in the cladding region of the fiber providingbetter solidifiability of the material, and also improves the spinningstability as well as the extensibility of the fibers. This leads to animprovement in the softness and/or feel of the spunbonded web, andfurthermore the drapability of the fibers or of a spunbonded webobtained from the fibers is improved.

In the context of the invention, it is advantageous if the difference inthe melting points of the first component and the second component is atmost 6° C. or between 1° C. to 8° C., preferably between 1° C. to 6° C.In these advantageous parameter ranges, the positive effects of thepresent invention occur significantly more strongly.

Preferably, the mass fraction of the component with the lower meltingpoint in the bicomponent fiber is at most 50%, further preferably atmost 25%, preferably at most 10%, in particular at most 5%. In thiscontext, the bicomponent fiber is particularly preferably a core-sheathfiber, with the component with the lower melting point forming thesheath.

Advantageously, the difference between the melt flow indices of thefirst component and the second component is less than or equal to 25g/10 min, with the melt flow indices (hereinafter MFIs) of the firstcomponent and the second component each being less than or equal to 50g/10 min. Preferably, the difference between the melt flow indices ofthe first component and the second component is less than or equal to 20g/10 min, particularly preferably 15 g/10 min, and/or the MFIs of thefirst component and the second component are each less than or equal to40 g/10 min. Such advantageous selection of the components according tothe criterion of their MFIs has, surprisingly, a positive effect in amanner similar to the selection of the components according to theinvention on the basis of their melting points.

The MFI is measured according to ISO 1133 with a test load of 2.16 kgand a test temperature of 230° C. The MFI is also referred to as themelt flow index or MFR. The MFI is also referred to as the melt flowindex or melt flow rate (MFR). It is determined according to ISO 1133 bymelting the material in a heatable cylinder and forcing it through adefined die by means of the test load. The MFI is a measure of theviscosity of the melt of the respective polymer-containing component.The viscosity, in turn, is related to the degree of polymerization,which corresponds to the average number of monomer units in eachmolecule of a polymer.

The positive influence of the advantageous differences of the MFIsmainly concerns the specific tensile strength and the specific nailpull-out force. These two characteristic values of a spunbonded nonwovenmade from the fibers can be improved by the advantageously selectedMFIs. It is even possible to increase both characteristic valuessimultaneously, but in any case one of the two characteristic values canbe improved without the other characteristic value deteriorating. Thisalso has a positive effect on the haptic properties. Thus, the specifictensile strength can be increased without negatively affecting softnessand the so-called “textile handle”. The term “textile handle” isunderstood to mean a feeling of touch that is perceived as pleasant.

Preferably, the mass fraction of the component with the higher MFI inthe bicomponent fiber is at most 50%, further preferably at most 25%,preferably at most 10%, in particular at most 5%. In this context, thebicomponent fiber is particularly preferably a core-sheath fiber, withthe component with the higher MFI forming the sheath.

Advantageously, the polymer of one of the two components has beenpolymerized with a metallocene catalyst and the polymer of the othercomponent has been polymerized with a Ziegler-Natta catalyst andsubjected to a subsequent visbreaking treatment Preferably, the polymeris a polyolefin, in particular polypropylene, polyethylene or theircopolymer or a mixture thereof. The other polymer is preferably alsopolyolefin or a polyolefin copolymer. It is particularly advantageous ifboth polymers are composed of the same monomer or are at leastpredominantly composed of the same monomer.

Metallocene catalysts are structurally uniform catalysts containingtransition metals coordinated by cyclopentadiene ligands. Such catalystsare described in detail in U.S. Pat. Nos. 5,374,696 and 5,064,802.Express reference is made to the related disclosure. The advantage ofthese catalysts is that the polymers prepared with these catalysts havea narrow molecular weight distribution. The narrow molecular weightdistribution results in nonwovens with high elongation at break. Here,the elongation at break is the elongation of the fibers that results atthe maximum of the breaking force applied when a nonwoven strip is torn.Most importantly, a narrow molecular weight distribution leads to anincrease in process reliability during the production of spunbondednonwovens. The frequency of spinning disturbances, such as fiberbreakage, is reduced. Furthermore, a higher draw of the fibers ispossible, higher spinning speeds can be achieved and the titers that canbe achieved are lower. Here, lower titers mean a higher fineness of thefibers and/or the yarns obtained from the fibers.

Another advantage of metallocene catalysts and/or polymers producedusing metallocene catalysts is that the residual content of the catalystin the polymer is very low. The residual content of the catalyst in thepolymer represents an impurity of the polymer and can cause theproperties of the polymer to be changed in an undesirable way. Forexample, discoloration may occur during processing of the polymer.

A disadvantage of the metallocene catalysts is their slightly higherprice compared to the Ziegler-Natta catalysts. Furthermore, thermalbonding of the fibers during nonwoven production can be impeded whenmetallocene catalysts are used. This can be the case if thepossibilities opened up by the use of metallocene catalysts to increasethe crystallinity and strength of the individual fibers through theirhigher stretchability are exploited to a high degree.

Ziegler-Natta catalysts are heterogeneous mixed catalysts containingorganometallic compounds of main group elements and transition metalcompounds. In particular, elements of the first to third main groups areused as main group elements. The transition metal compounds contain, inparticular, metals of the titanium group. A large number of variants ofthese catalysts exist. For the purposes of the present invention, theZiegler-Natta catalysts are defined essentially by their distinctionfrom the metallocene catalysts.

Although the Ziegler-Natta catalysts are less expensive than themetallocene catalysts, the poylmers produced with the Ziegler-Nattacatalysts have a significantly broader molecular weight distributionthan polymers produced with metallocene catalysts. To improve thestretchability of the fibers, which serves in particular to increaseprocess reliability, the polymers produced with Ziegler-Natta catalystsare therefore usually posttreated. This post-treatment is referred to as“visbreaking”. During the visbreaking treatment, polymer chains arecleaved, reducing the molecular weight of the individual molecules andincreasing the number of molecules. This also reduces the width of themolecular weight distribution. The cleavage of polymer chains is broughtabout by heat, irradiation, the addition of peroxide or similarmeasures. Examples of such visbreaking treatments are described in U.S.Pat. Nos. 4,282,076 and 5,723,217, among others.

However, such visbreaking treatment cannot achieve the narrow molecularweight distribution of polymers produced with metallocene catalysts, northe good stretchability of fibers obtained from these polymers. Also,polymers produced with Ziegler-Natta catalysts have a higher content ofimpurities than polymers produced with metallocene catalysts. This isdue, on the one hand, to the fact that a comparatively higher catalystcontent is required when producing the polymer with a Ziegler-Nattacatalyst, which necessitates a comparatively higher proportion ofcatalyst residues in the polymer, and, on the other hand, to auxiliariesthat are added as part of the visbreaking treatment, as a result ofwhich they represent an additional source of impurities in the finishedpolymer.

The advantage of polymers produced using Ziegler-Natta catalysts withsubsequent visbreaking treatment is mainly their low price and highavailability on the market. Another advantage is the good thermalbondability of the fibers produced from these polymers.

Surprisingly, it has now been shown that the advantageous selection ofpolymers on the basis of the catalysts used in their production meansthat the resulting bicomponent fibers allow a combination of theadvantages of using the respective catalyst types. Thus, it is possibleto reduce the costs compared to the use of pure polymer fibers producedby means of metallocene catalysts, while at the same time realizing theadvantages of using metallocene catalysts. In addition, betterbondability of the fibers can be achieved compared to fibers made frompolymers produced exclusively using metallocene catalysts.

Preferably, the mass fraction of the component whose polymer has beenpolymerized with a metallocene catalyst in the bicomponent fiber is atmost 50%, further preferably at most 25%, preferably at most 10%, inparticular at most 5%. The bicomponent fiber is particularly preferablya core-sheath fiber, with the component whose polymer has beenpolymerized with a metallocene catalyst forming the sheath.

Advantageously, the first polymer and/or the second polymer is apolyolefin or a polyolefin copolymer, preferably a polymer and/orcopolymer of ethylene, propylene, butylene, hexene or octene and/or amixture and/or a blend thereof. It has been shown that these polymersare particularly well suited for producing the bicomponent fibersaccording to the invention therefrom. In this context, a copolymer is tobe understood as a polymer prepared from at least two different types ofmonomers, the mass fraction of the monomer which is decisive for thedesignation of the copolymer being at least 50%.

Preferably, the first polymer and/or the second polymer may bepolyethylene terephthalate (PET) and/or a polyethylene terephthalatecopolymer, in particular, the first polymer and/or the second polymerconsists of PET and/or Co-PET.

Particularly preferred for the bicomponent fiber is a materialcomposition for the first and second components of polypropylene and/orpolyethylene and polyethylene terephthalate and/or polyethyleneterephthalate copolymer. Here, either the first or the second polymermay comprise and/or consist of polyproplyene and/or polyethylene.Depending on whether the first or second polymer comprises PP and/or PE,the second or first polymer not comprising PP and/or PE comprises and/orconsists of PET and/or Co-PET. Consequently, if the first polymercomprises PP and/or PET, the second polymer comprises PET and/or Co-PETand vice versa.

Preferably, the bicomponent fiber is a core-sheath fiber, wherein themass fraction of the core is 50% to 98%, preferably 60% to 95%, morepreferably 70% to 95%, most preferably 80% to 90%. It has been shownthat the advantages of the bicomponent fiber according to the invention,when it is a core-sheath fiber, occur to a particular extent with theseadvantageous mass fractions of the core.

If the bicomponent fiber is a side-by-side fiber, segmented-pie fiber orislands-in-the-sea fiber, the mass ratio of the two components is in therange from 10:90 up to 90:10, preferably in the range from 70:30 up to30:70, particularly preferably in the range from 60:40 up to 40:60. Forthese fiber types, it has been shown that the advantages of thebicomponent fiber according to the invention can be achievedparticularly well for the listed component ratios.

In another preferred embodiment, the bicomponent fiber is a multilobal,in particular a tetralobal or trilobal fiber. Due to theircross-sectional geometry, these fibers offer a higher specific surfacearea than comparable fibers with circular cross-sections. In combinationwith these, the advantages of the fibers according to the invention canbe exploited particularly efficiently, especially when the differentproperties of the components to be optimized by the bicomponent fiberaccording to the invention are properties that affect the surface of thefiber.

Advantageously, the diameter of the bicomponent fiber is between 1 μmand 50 μm, preferably between 5 μm and 30 μm, particularly preferablybetween 8 μm and 20 μm. It has been shown that especially with fiberdiameters in these advantageous ranges, the combination of twocomponents in a bicomponent fiber leads to synergy effects to aparticular extent.

In particular, the outer protective layer and/or the inner protectivelayer is formed as a spunbonded fabric with bicomponent fibers accordingto the invention. The spunbonded fabric can have the advantages and/orproperties described below.

By using the bicomponent structure of the inner and/or outer protectivelayer formed as a nonwoven layer, a higher strength, in particular astrength improved by up to 20%, can be achieved compared to apolypropylene spunbond. Furthermore, very good weathering stabilityproperties, in particular improved UV and hydrolysis properties, can beprovided.

Two properties that play a special role in spunbonded nonwovens are thespecific tensile strength of the spunbonded nonwoven and the specificnail pull-out force of the spunbonded nonwoven. A desirable highspecific tensile strength is achieved by fibers with high strength.

Good bondability in this sense means that the mobility of the fibers inthe spunbonded web can be adjusted as defined as possible during thebonding of the fibers during the production of a spunbonded web. Thespecific adjustment of the mobility of the fibers in the nonwoven, whichdepends on the strength of the bond between the fibers, is theprerequisite for producing a spunbonded nonwoven with high specifictensile strength and simultaneously high specific nail pull-out force.

In practice, there may be the problem that suitable fibers with highstrength have poor bondability and fibers with good bondability onlyhave low strength. Therefore, especially in the case of the productionof a spunbonded nonwoven, which is to have both a high specific tensilestrength and a high specific nail pull-out strength, the use of abicomponent fiber is useful. The bicomponent fibers of the invention areparticularly suitable for achieving a high specific tensile strength anda high specific nail pull-out force of a spunbonded nonwoven, since thebicomponent fibers of the invention can be optimized with respect to acombination of good bonding properties and high strength.

Such a nonwoven fabric made from the fibers of the invention is suitablefor numerous applications, for example in medicine, in the hygienesector, in the automotive industry, in the clothing sector, in home andtechnical textiles, and in particular in the construction sector andagriculture. According to the invention, the field of application of thenonwoven overlaps with the field of application of the composite film.Possible applications further include use in filters and membranes,battery separators, and as a support nonwoven for laminates and as acarrier for coatings of all kinds.

Advantageously, the specific breaking force of the spunbonded web is atleast 1.8 N/g·5 cm in machine direction and/or at least 1.3 N/g·5 cm intransverse direction, preferably 2.0 N/g·5 cm in machine directionand/or at least 1.5 N/g·5 cm in transverse direction, preferably atleast 2.2 N/g·5 cm in machine direction and/or at least 2.0 N/g·5 cm intransverse direction, particularly preferably at least 2.4 N/g·5 cm inmachine direction and/or at least 1.9 N/g·5 cm in transverse direction.The specific tensile strength is measured according to EN 12311-1.

It has been shown that these advantageous minimum values for thespecific tear strength of the spunbonded web should be aimed for in anycase if bicomponent fibers according to the invention are used for theproduction of the spunbonded web. The bicomponent fibers according tothe invention make it possible to achieve these advantageous minimumvalues for the specific tensile strength without a disproportionate dropin the specific nail pull-out force.

Advantageously, the specific nail pull-out force of the spunbonded webis at least 1.0 N/g in machine direction and/or at least 1.2 N/g intransverse direction, preferably at least 1.4 N/g in machine directionand/or at least 1.5 N/g in transverse direction, preferably at least 1.6N/g in machine direction and/or at least 1.8 N/g in transversedirection, particularly preferably at least 1.8 N/g in machine directionand/or at least 2.1 N/g in transverse direction.

The specific nail pull-out force is the maximum force that occurs duringthe tearing of a nonwoven strip when the nonwoven strip already has agiven damage, namely a nail pierced through the nonwoven fabric. Thespecific nail pull-out force is measured according to EN 12310-1. It hasbeen shown that the minimum values mentioned for the specific nailpull-out force of the spunbonded nonwoven can be aimed at without thespecific tear-out force of the spunbonded nonwoven droppingdisproportionately if bicomponent fibers according to the invention areoptimized accordingly with respect to their bondability and strength. Inparticular, it is also possible to realize a combination of theabove-mentioned specific advantageous nail tear-out forces and theabove-mentioned advantageous specific minimum tear-out forces.

The combination of these two advantageous minimum parameters results ina spunbonded web that is suitable for a wide range of applications interms of its mechanical properties. Such a spunbonded web can, forexample, be used well in the construction sector, where it must often bepossible to fasten the spunbonded webs by nailing, stapling or screwing.The spunbonded web must not tear off or tear out when it is fastened toa roof, for example. It is also quite possible to use these advantageousspunbonded webs as geotextiles. In any case, geotextiles must have ahigh tolerance for punctual damage, such as that caused by sharp stones.

In practice, high specific nail pull-out strength often goes hand inhand with good haptics. The softness and textile feel of such spunbondednonwovens and the composite films therefore also open up applications,e.g. applications in the hygiene or medical sectors. The reason for thegood feel is the high mobility of individual fibers, which is regularlyaccompanied by the occurrence of high nail pull-out forces. In practice,fibers that behave in this way also regularly exhibit haptic propertiesthat are perceived as soft and pleasant. Fiber segment mobility allowsfibers to “collect” in the nail as the nail moves through the nonwovenby avoiding the nail moving through the nonwoven and not tearingimmediately. This results in a zone of increased fiber density, i.e. azone of increased strength, around the nail.

Furthermore, the present invention relates to the use of a compositefilm according to one of the embodiments described above as aconstruction film, facade membrane, building envelope and/or roofingmembrane and/or for use in the construction industry.

In order to avoid unnecessary repetition, reference is made to theprevious embodiments, advantages and/or preferred embodiments, whichapply in the same way to the use according to the invention.

Furthermore, it is understood that any intermediate intervals andindividual values are included in the aforementioned intervals and rangelimits and are to be considered disclosed as essential to the invention,even if these intermediate intervals and individual values are notspecifically indicated.

Further features, advantages and possible applications of the presentinvention will be apparent from the following description of examples ofembodiments based on the drawing and the drawing itself. In thiscontext, all the features described and/or illustrated constitute,individually or in any combination, the subject-matter of the presentinvention, irrespective of their summary in the claims and theirrelation back.

It shows:

FIG. 1 a schematic cross-sectional view of the composite film accordingto the invention,

FIG. 2 schematic cross-sectional view of a further embodiment of thecomposite film according to the invention,

FIG. 3 schematic cross-sectional view of a further embodiment of thecomposite film according to the invention,

FIG. 4 schematic cross-sectional view of a further embodiment of thecomposite film according to the invention,

FIG. 5 schematic cross-sectional view of a further embodiment of thecomposite film according to the invention,

FIG. 6 schematic cross-sectional view of a further embodiment of thecomposite film according to the invention,

FIG. 7 a schematic cross-sectional view of a further embodiment of thecomposite film according to the invention,

FIG. 8 schematic and perspective cross-sectional view of a furtherembodiment of the composite film according to the invention,

FIG. 9 schematic cross-sectional view of a further embodiment of thecomposite film according to the invention,

FIG. 10 schematic cross-sectional view of a further embodiment of thecomposite film according to the invention,

FIG. 11 cross-sectional view of an embodiment of a bicomponent fiberaccording to the invention as a core-sheath fiber,

FIG. 12 cross-sectional view of an embodiment of a bicomponent fiberaccording to the invention as a core-sheath fiber with a thin sheath,

FIG. 13 cross-sectional view of a further embodiment of a bicomponentfiber according to the invention as a core-sheath fiber with aneccentrically arranged core, and

FIG. 14 part of an exemplary spunbonded web according to the invention.

FIG. 1 shows a composite film 1 with an outer protective layer 3 and aninner protective layer 4. A functional layer 2 is arranged between theouter protective layer 3 and the inner protective layer 4. The compositefilm 1 shown is intended for use in the construction industry and foruse as a construction film, in particular for covering buildings and/orfor use as a roofing membrane.

The functional layer 2 shown in FIG. 1 is designed as at least asingle-layer membrane layer. The outer protective layer 3 and the innerprotective layer 4 are formed as nonwoven layers comprising polyolefin.In the embodiment example shown in FIG. 1, the outer protective layer 3has at least one bicomponent fiber 5 (not shown, see FIG. 14)—in theembodiment example shown, a plurality of bicomponent fibers 5. Thebicomponent fiber 5 has a first component 6 and a second component 7,the first component 6 having a first polymer and the second component 7having a second polymer as a constituent. The first polymer and thesecond polymer may be different from each other in the illustratedembodiment.

In particular, the outer protective layer 3 and/or the inner protectivelayer 4 can be firmly bonded and/or fully bonded to the functional layer2.

In another embodiment not shown, it is provided that the first polymercomprises polypropylene, in particular polymerized by a Ziegler-Nattacatalyst, and the second polymer comprises polypropylene, in particularproduced by metallocene catalysts, or vice versa.

In the embodiment example shown in FIG. 2, it is provided that the innerprotective layer 4 comprises the at least one bicomponent fiber 5. Infurther embodiments, both the outer protective layer 3 and the innerprotective layer 4 can be formed as a nonwoven layer comprisingbicomponent fibers 5.

Insofar as the composite film 1 is used for weather protection of goods,the topside 12 may face the weather side or the weather, whereas theunderside 13 may face the interior of a building, for example. Thetopside 12 is arranged on the outer side of the outer protective layer3. The underside 13 is provided on the opposite outer side of thecomposite film 1. In principle, it is also possible not to expose thecomposite film 1 to the weather, in which case the underside 13 may facethe goods, material or the like to be covered.

The functional layer 2 shown in FIG. 1 is designed as a monolithicmembrane layer. A monolithic membrane layer is a selectively permeablemembrane layer that is pore-free or closed-cell.

The functional layer 2 has plastic and/or synthetic resin as thematerial. In particular, an elastomeric material and/or a thermoplasticmaterial is provided. In the embodiment example shown in FIG. 1, thefunctional layer 2 has a polyurethane plastic. In the embodiment exampleshown, the polyurethane plastic of the functional layer 2 is athermoplastic polyurethane (TPU). In further embodiments, the functionallayer 2 may not only comprise the thermoplastic polyurethane, but mayalso comprise it.

In addition, the functional layer 2 shown in FIG. 1 has a basis weightor grammage of less than 100 g/m². In particular, the basis weight ofthe functional layer 2 is between 5 g/m² and 25 g/m².

FIG. 2 shows that the functional layer 2 has at least two layers ofmembrane layers—that is, two membrane layers 8. In the embodimentexample shown, the membrane layers 8 are formed differently from oneanother and have, in particular, a different material composition and/ora different grammage.

In particular, the membrane layers 8 are firmly bonded to each other,proferably via a full-surface adhesive bond.

FIG. 3 shows that the functional layer 2 has a three-layer structureconsisting of three membrane layers 8. In the embodiment example shown,the outer membrane layers 9 are of identical design and include acentral membrane layer 8 having a different material composition and/orsurround a central membrane layer 8. The identical design of the outermembrane layers 9 is to be understood as meaning that they have at leastsubstantially the same material composition, the same material and/orthe same material properties. In particular, the outer membrane layers 9have the same functional design. In a further, not shown embodimentexample, it can be provided that the membrane layers 8 differ from eachother, so that also the outer membrane layers 9 are formed differentlyfrom each other.

In an embodiment not shown, the outer membrane layers 9 are identical,with the topside 12 and the underside 13 being functionally identical,in particular with the outer protective layer 3 being identical and/orfunctionally identical to the inner protective layer 4.

In another embodiment not shown, the composite film 1 has a symmetricalstructure.

The outer membrane layer 9 is to be understood as the membrane layer 8directly facing the outer protective layer 3 or the inner protectivelayer 4.

The functional layer 2 shown in FIG. 3 is designed in such a way that atleast one membrane layer 8 comprises thermoplastic copolyester (TPEE)and/or thermoplastic polyurethane (TPU) as material and/or consiststhereof. In particular, the outer membrane layer 9 has thermoplasticcopolyester and/or thermoplastic polyurethane. In a further, not shownembodiment example, the functional layer 2 is formed of TPEE layersand/or TPU layers, wherein the layers can be firmly bonded to eachother.

It is not shown that at least one outer membrane layer 9 and/or theinner membrane layer 8 of the multilayer functional layer 2 comprisesand/or is formed from a foamed polymer. The outer membrane layer 9comprising the foamed polymer can be bonded to the protective layerfacing it—that is, either the outer protective layer 3 or the innerprotective layer 4—by means of bonding. In particular, the outer-sidemembrane layer 9 comprising the foamed polymer penetrates the surfaceregion or the outermost surface layer of the outer protective layer 3and/or the inner protective layer 4. The interlocking may be achieveddue to the manufacturing process of the composite film 1, in particulardue to the slowed cooling caused due to the foaming of the outer-sidemembrane layer 9. Furthermore, the outer membrane layer 9 is also firmlybonded to the immediately adjacent membrane layer 8, wherein thisbonding can also be caused by interlocking.

Furthermore, FIG. 3 shows that the outer protective layer 3 is formed asa nonwoven layer comprising polypropylene. In particular, the outerprotective layer 3 is formed as a polypropylene needle-punched nonwovenlayer—that is, a nonwoven layer consolidated by needle-punching. Infurther embodiments not shown, the inner protective layer 4 canadditionally or alternatively be formed as a nonwoven layer comprisingand/or consisting of polypropylene, in particular a polypropylene needlepunched nonwoven layer.

FIG. 4 shows that the outer protective layer 3 and the inner protectivelayer 4 are formed as a spunbonded layer. In further embodiments, whichare not shown, either the outer protective layer 3 or the innerprotective layer 4 can be formed as a spunbonded layer. FIG. 14 showsthe outer protective layer 3 in the form of a spunbonded layer, which isalso composed of bicomponent fibers 5 each having a first component 6and a second component 7.

In the embodiments shown in FIGS. 1 to 5, the outer protective layer 3and the inner protective layer 4 have a grammage of less than 250 g/m².In particular, the grammage of the outer protective layer 3 and/or theinner protective layer 4 is between 30 g/m² and 100 g/m².

In principle, various consolidation methods, such as mechanical,chemical and/or thermal consolidation, can be provided for consolidatingthe outer protective layer 3 and the inner protective layer 4. FIG. 5shows a thermally consolidated outer protective layer 3.

FIG. 4 shows that the functional layer 2 is firmly connected to theouter protective layer 3 and the inner protective layer 4. The fixedconnection of the functional layer 2 to the protective layers 3, 4 isprovided over the entire surface via the connecting surfaces. In furtherembodiments, a partial-surface connection of the functional layer 2 tothe outer protective layer 3 and/or the inner protective layer 4 mayalso be provided. In addition, FIG. 4 shows that the functional layer 2is bonded to both the outer protective layer 3 and the inner protectivelayer 4. The bonding and/or adhesive layer and/or adhesion-promotinglayer 10 or bonding layer is designed in particular in such a way thatthe composite film is and/or remains open to diffusion, in particularwherein a very thin adhesive layer application and/or a screenapplication of the adhesive is carried out.

For bonding the functional layer 2 to the protective layers 3, 4, anadhesion-promoting layer 10 is provided, which comprises an adhesionpromoter polymer. FIGS. 4 to 6 show the different arrangement of theadhesion-promoting layer 10. For example, the adhesion-promoting layer10—as shown in FIG. 5—can be formed as part of the functional layer 2and/or the adhesion promoter polymer penetrates at least in some areasinto the surfaces of the functional layer 2 facing the protective layers3, 4.

FIG. 4 shows that the adhesion-promoting layer 10 is formed as aseparate layer provided between the functional layer 2 and theprotective layers 3, 4. This adhesion-promoting layer 10 can be appliedto the protective layers 3, 4 and/or to the functional layer 2 duringthe manufacturing process of the composite film 1.

FIG. 6 again shows that the adhesion-promoting layer 10 is formed aspart of the protective layers 3, 4. Thus, FIG. 6 shows that the adhesionpromoter polymer has penetrated into the surface areas of the protectivelayers 3, 4 facing the functional layer 2.

In particular, the adhesion-promoting layer 10 is provided as acomponent of the protective layer or protective layers 3, 4 comprisingthe bicomponent fibers 5. The adhesion-promoting layer 10 is firmlybonded to the functional layer 2 or the protective layers 3, 4, inparticular over the entire surface. The adhesion promoter polymer or thematerial of the adhesion-promoting layer 10 may be a plastic and/or asynthetic resin, preferably polyurethane.

The composite film 1 shown in FIG. 6 is designed to be permeable towater vapor, open to diffusion and rainproof. In further embodiments,the composite film 1 may be water vapor permeable, diffusion open,windproof, rainproof, water repellent and/or waterproof. The compositefilm 1 shown in FIG. 6 has an Sd value of less than or equal to 0.5 m.In further embodiments, the Sd value of the composite film 1 may bebetween 0.01 m to 0.1 m. The Sd value of the composite film 1 is suchthat the diffusion-open properties of the composite film 1 and/or thefunctional layer 2 can be adequately ensured.

Furthermore, in the embodiment shown in FIG. 6, the composite film 1 hasa tear strength of greater than 50 N/mm. In further embodiments, thetear strength of the composite film 1 may be between 100 N/mm to 300N/mm. In the embodiment example shown in FIG. 6, the tear propagationstrength of the composite film 1 is greater than 50 N/mm. In furtherembodiments not shown, the tear propagation strength of the compositefilm 1 is between 100 N/mm to 300 N/mm.

FIG. 7 shows that a reinforcing layer 11 is introduced in the layerstructure of the composite film 1. In the illustrated embodimentexample, the reinforcing layer 11 is arranged between the outerprotective layer 3 and the functional layer 2. In further embodimentsnot shown, the reinforcing layer 11 may be arranged between the innerprotective layer 4 and the functional layer 2. The reinforcing layer 11is formed as a leno fabric. Furthermore, the reinforcing layer 11 maycomprise and/or consist of plastic and/or synthetic resin as thematerial. In particular, the reinforcing layer 11 has and/or consists ofa plastic polymer, such as polypropylene (PP) and/or polyethyleneterephthalate (PET).

FIGS. 8 to 10 show that the composite film 1 has at least onelongitudinal edge-side adhesive zone 14. The longitudinal edge-sideadhesive zone 14 is provided on the topside 12 and/or on the underside13 of the composite film 1. FIG. 8 shows that the longitudinal edge-sideadhesive zone 14 is spaced from the longitudinal edge 15 of thecomposite film 1.

It is not shown that the adhesive zone 14 is strip-shaped. Furthermore,it is not shown that the adhesive zone 14 can also be formed asinterrupted strips.

The width of the adhesive zone 14 in the illustrated embodiment isbetween 2 to 10 cm.

FIG. 8 shows that in each case one adhesive zone 14 is provided on thetopside 12 and on the underside 13. FIG. 9 shows that in each case twolongitudinal edge-side adhesive zones 14 are provided both on theunderside 13 and on the topside 12 of the composite film 1. FIG. 10shows that two longitudinal edge-side adhesive zones 14 are provided onthe underside 13.

In FIG. 8, the adhesive zone 14 is arranged in a longitudinal edgeregion, which comprises the longitudinal edge 15, of the topside 12 andthe underside 13 of the composite film 1. In the embodiment exampleshown in FIG. 8, the longitudinal edge region extends from thelongitudinal edge 15 of the composite film 1 over or greater than 1% ofthe width of the composite film 1, in the embodiment example shown overabout 15%+/−10% of the width of the composite film 1. FIGS. 8 to 10 onlyschematically show the arrangement of the adhesive zones 14 and do notserve to draw conclusions for the dimensions for the lengths or widthsof the adhesive zone 14.

The adhesive zones 14 shown in the illustrated embodiments are formedsuch that when adjacent composite films 1 are bonded together,wind-tight and/or airtight bonding occurs.

The offset of the adhesive zones 14 shown in FIG. 8 is selected in sucha way that, when adjacent composite films 1 are bonded, anadhesive-in-adhesive bond is produced between the adhesive zones 14 ofadjacent rows of the composite film 1. In the case of the laid compositefilm 1, it is provided that the adhesive zones 14 are arranged one abovethe other, at least in certain regions, so that an adhesive-in-adhesivebond is produced between the adhesives of the adhesive zones 14.Ultimately, it may be provided that different adhesives and/or adhesiveproperties, such as grammage and/or width of the adhesive application,are provided for different adhesive zones 14, it being preferred thatthe adhesive zones 14 are identical with respect to the adhesive usedand all adhesive properties.

It is not shown that the mating surface for the adhesive zone 14comprising the adhesive is covered with a liner and/or surface-treated.In particular, it is not shown that the adhesive zone 14 may be coveredby a lacquer. The liner may serve to protect the adhesive zone 14, inparticular from impurities and/or from contamination.

FIGS. 11 to 13 show cross-sectional views of exemplary bicomponentfibers 5 according to the invention. The bicomponent fibers 5 shown eachhave a first component 6 and a second component 7. In the case of thecore-sheath fibers shown in FIGS. 11 to 13, the first component 6surrounds the second component 7 and thus forms the outer surface of thebicomponent fiber 5. In cross section, the bicomponent fibers 5 shownhave an at least approximately circular and/or round geometry. Infurther embodiments not shown, the bicomponent fiber 5 may also havenon-circular cross-sections, for example a trilobal cross-section orother multilobal cross-sections. In the case of a very thin sheath ofthe bicomponent fiber 5 surrounding the second component 7, the sheathmay well have defects. That is, the sheath does not completely surroundthe core, but is broken in some places, so that the core also forms theouter surface of the fiber in these places. Such fibers are also“core-sheath fibers”. In particular, in such fibers, the componentforming the openwork sheath forms the outer surface of the fiber withinthe meaning of the present invention.

Not shown is that the bicomponent fiber 5 may also be formed as aside-by-side fiber. Side-by-side fibers may be characterized in thatboth the first component 6 and the second component 7 form part of theouter surface of the bicomponent fiber 5. Circular or at leastapproximately circular cross-sections are also possible for side-by-sidefibers, as are multilobal cross-sections. Depending on which fiberproperties and/or nonwoven properties are to be achieved, the firstcomponent 6 and the second component 7 can be combined in differentratios in different spatial arrangements relative to one another.

Also not shown is that the bicomponent fiber 5 may also be formed as asegmented-pie fiber. This fiber structure has a relationship toside-by-side fiber structures in that both the first component 6 and thesecond component 7 can form part of the outer surface of the bicomponentfiber 5.

Also, a design of the bicomponent fiber 5 as an Island-In-The-Seastructure as a modification of a core-cladding fiber is not provided inthe embodiments shown. In an Island-In-The-Sea structure of thebicomponent fiber 5, a plurality of cores from the second component 7may be present. The individual cores from the second component 7 aresurrounded by a common sheath from the first component 6.

Furthermore, mixed forms between core-sheath fibers and side-by-sidefibers are possible in principle.

FIG. 14 shows how a plurality of exemplary bicomponent fibers 5 form aspunbonded fabric. In the embodiment shown, the spunbonded fabric isformed as an outer protective layer 3. The inner protective layer 4 canalso be formed as a spunbonded fabric shown in FIG. 14. In this case,the spunbonded fabric forms a web with a transverse direction X, athickness direction Y and a length direction Z, which is also referredto as the machine direction.

An exemplary spunbonded fabric may be made from bicomponent fibers 5that have been thermally bonded by means of a calendar. In theillustrated embodiment example, the bicomponent fibers 5 are core-sheathfibers having a sheath of the first component 6 with polypropylene asthe first polymer with a core of the second component 7 with apolypropylene as the second polymer. The grammage of the spunbonded webshown in FIG. 14 may be 70 g/m²+/−20 g/m².

Not shown is that the difference in the melting point of the firstcomponent 6 and the second component 7 is less than or equal to 8° C. Inparticular, the difference in the melting points of the first component6 and the second component 7 can range from 1° C. to 6° C.

Furthermore, it is not shown that the melt flow indices of the firstcomponent 6 and the second component 7 are less than or equal to 25 g/10min. In addition, the melt flow indices of the first component 6 and thesecond component 7 can each be less than or equal to 50 g/10 min.

In particular, the component with the low melting point in thecross-section of the bicomponent fiber 5 may form the outer surface ofthe bicomponent fiber 5, in particular surrounding preferablycompletely, the component with the higher melting point.

The polymer of one of the two components 6, 7 may have been polymerizedwith a metallocene catalyst. The polymer of the other component may havebeen polymerized with a Ziegler-Natta catalyst and subsequentlysubjected to a visbreaking treatment.

Furthermore, it is not shown that the first component 6 comprises anadditive, wherein the mass fraction of the additive in the secondcomponent 7 is smaller than in the first component 6, preferably at most66.6%.

The additive may be a primary or secondary antioxidant, a UV absorber, aUV stabilizer, a flame retardant, an antistatic agent, a lubricant, ametal deactivator, a hydrophilizing agent, a hydrophobizing agent, ananti-fogging additive, and/or a biocide.

Where appropriate, the additive may be selected from the groupconsisting of:

-   -   Sterically hindered phenols, aromatic secondary or tertiary        amines, aminophenols, aromatic nitro or nitroso compounds,        organic phosphites or phosphonates, thioethers, thioalcohols,        thioesters, sulfides and sulfur-containing organic acids,        dithiocarbamates, thiodipropionates, aminopyrazoles,        metal-containing chelates, mercaptobenzimidazoles,        hydroxybenzophenones, cinnamates, oxalanilides, salicylates,        resorcinol monobenzoates, benzotriazoles, triazines,        benzophenones, titanium dioxide, carbon black, metal-containing        complexes of organic sulfur or phosphorus compounds, sterically        hindered amines (HALS), metal hydroxides, borates, organic        bromine- or chlorine-containing compounds, organic phosphorus        compounds, antimony trioxide, melamine, melamine cyanurate,        expandable graphite or other intumescent systems, quaternary        ammonium salts, alkyl sulfonates, alkyl sulfates, alkyl        phosphates, dithiocarbamates, (alkaline earth) metal        carboxylates, polyethylene glycols and their esters and ethers,        ethoxylates, mono- and diglycerides, fatty alcohols, esters of        fatty alcohols, fatty acids, fatty acid esters, dicarboxylic        acid esters, fatty acid amides, metal salts of fatty acids,        polyolefin waxes, natural or artificial kerosenes and        derivatives thereof, fluoropolymers and fluoroligomers,        antiblocking agents such as silicas, silicones, silicates,        calcium carbonate, amides of mono- and dicarboxylic acids and        their derivatives, cyclic amides, hydrazones and bishydrazones,        hydrazides, hydrazines, melamine and its derivatives,        benzotriazoles, aminotriazoles, sterically hindered phenols in        combination with complexing metal compounds, benzylphosphonates,        pyridithiols, thiobisphenol esters, polyglycols, ethoxylates,        fluoropolymers and fluoroligomers montan waxes, in particular        stearates, 10,10′-oxybisphenoxarsine (OBPA),        N-(trihalogen-methyl-thiol)phthalimide, tributyltin oxide, zinc        dimethyldithiocarbamate, diphenylantimony-2-ethylhexanoate,        copper-8-hydroxyquinoline, isothiazolones, silver and silver        salts as biocides or mixtures thereof.

Furthermore, it is not shown that the first polymer and/or the secondpolymer is a polyolefin or a polyolefin copolymer, preferably a polymerand/or copolymer of ethylene, propylene, butylene, hexene or octeneand/or a mixture and/or a blend thereof, and/or a polyethyleneterephthalate and/or a polyethylene terephthalate copolymer.

The mass fraction of the component with the low melting point in thebicomponent fiber 5 can be at most 50%.

LIST OF REFERENCE SIGNS

-   1 Composite film-   2 Functional layer-   3 outer protective layer-   4 inner protective layer-   5 Bicomponent fiber-   6 first component-   7 second component-   8 Membrane layer-   9 external membrane layer-   10 Adhesion-promoting layer-   11 Reinforcement layer-   12 Topside-   13 Underside-   14 Adhesive zone-   15 Longitudinal edge

The invention claimed is:
 1. A composite construction film comprising:at least one functional layer, at least one outer protective layer andat least one inner protective layer, the functional layer being arrangedbetween the outer protective layer and the inner protective layer,wherein the composite film is open to diffusion, the at least onefunctional layer includes thermoplastic polyurethane (TPU), the at leastone functional layer is formed as at least a single-layer membranelayer, that the outer protective layer and the inner protective layerare formed as a nonwoven layer comprising polyolefin, and in that theouter protective layer and/or the inner protective layer comprises atleast one bicomponent fiber with a first component and a secondcomponent, the first component comprising a first polymer and the secondcomponent comprising a second polymer.
 2. The composite film accordingto claim 1, wherein the at least one functional layer is a monolithicmembrane layer.
 3. The composite film according to claim 1, wherein theat least one functional layer comprises one or more of: plastic,synthetic resin, an elastomeric material, a thermoplastic material,and/or a polyurethane plastic.
 4. The composite film according to claim1, wherein the at least one functional layer has a grammage of: lessthan 100 g/m², between 1 g/m² to 70 g/m², between 3 g/m² to 40 g/m²,between 4 g/m² to 30 g/m² or between 5 g/m² to 25 g/m².
 5. The compositefilm according to claim 1, wherein the at least one functional layercomprises at least two membrane layers, wherein the at least twomembrane layers are formed differently or the at least two membranelayers are formed at least substantially identically.
 6. The compositefilm according to claim 1, wherein at least one membrane layer of the atleast one functional layer, that is an outer membrane layer facing theouter protective layer and/or inner protective layer, includesthermoplastic copolyester (TPEE) and/or thermoplastic polyurethane (TPU)and/or the at least one functional layer is formed from TPEE layersand/or TPU layers.
 7. The composite film according to claim 1, whereinat least one outer membrane layer and/or one inner membrane layer of theat least one functional layer comprises a foamed polymer, wherein the atleast one outer membrane layer is bonded to the outer and/or innerprotective layer.
 8. The composite film according to claim 1, whereinthe at least one outer protective layer and/or the at least one innerprotective layer is formed as a nonwoven layer comprising polypropyleneor as a polypropylene needlefelt layer.
 9. The composite film accordingto claim 1, wherein the at least one outer protective layer and/or theat least one inner protective layer is formed as a spunbonded layer. 10.The composite film according to claim 1, wherein the grammage of the atleast one outer protective layer and/or of the at least one innerprotective layer is: less than or equal to 250 g/m², between 1 g/m² and250 g/m², between 10 g/m² and 150 g/m², between 20 g/m² and 120 g/m², orbetween 30 g/m² and 100 g/m².
 11. The composite film according to claim1, wherein the at least one outer protective layer and/or the at leastone inner protective layer is formed as a mechanically, chemicallyand/or thermally, consolidated nonwoven layer.
 12. The composite filmaccording to claim 1, wherein the at least one functional layer isfirmly bonded, or glued, to the outer protective layer and/or the innerprotective layer.
 13. The composite film according to claim 1, whereinthe at least one outer protective layer and/or the at least one innerprotective layer, comprising the at least one bicomponent fiber, and/oran outer functional layer, has an adhesion-promoting layer comprising apolymer, wherein the adhesion-promoting layer is firmly bonded to thefunctional layer and/or wherein the adhesion-promoting layer comprises aplastic and/or a synthetic resin, and/or a polyurethane.
 14. Thecomposite film according to claim 1, wherein the composite film ispermeable to water vapor, windproof, rainproof, water-repellent and/orwaterproof, and wherein the composite film has an Sd value of: less thanor equal to 0.5 m, 0.008 m to 0.5 m, 0.009 m to 0.2 m, or 0.01 m to 0.1m.
 15. The composite film according to claim 1, wherein the tearstrength of the composite film is: greater than 50 N/mm, between 50 N/mmto 600 N/mm, or between 100 N/mm to 400 N/mm, and/or that the tearpropagation strength of the composite film is: greater than 50 N/mm,between 50 N/mm and 500 N/mm, or between 100 N/mm to 300 N/mm.
 16. Thecomposite film according to claim 1, wherein at least one reinforcinglayer is arranged between the at least one functional layer and the atleast one outer protective layer and/or the at least one innerprotective layer, the reinforcing layer being a leno fabric, thereinforcing layer comprising a plastic and/or synthetic resin, a plasticpolymer, a polypropylene (PP) and/or polyethylene terephthalate (PET).17. The composite film according to claim 1, wherein at least onelongitudinal-edge-side adhesive zone is provided on a topside and/or anunderside of the composite film, the longitudinal-edge-side adhesivezone being spaced apart from a longitudinal edge of the composite film,and/or the adhesive zone being in the form of strips or as interruptedstrips, and/or the adhesive zone having a width of between 2 and 10 cm.18. The composite film according to claim 1, wherein a difference inmelting points of the first component and the second component is lessthan or equal to 8° C., wherein the difference in the melting points ofthe first component and the second component is at most 6° C., between1° C. to 8° C., or between 1° C. to 6° C.
 19. The composite filmaccording to claim 1, wherein a difference between melt flow indices ofthe first component and the second component is: less than or equal to25 g/10 min, less than or equal to 20 g/10 min, or 15 g/10 min.
 20. Thecomposite film according to claim 1, wherein melt flow indices of thefirst component and the second component are each less than or equal to50 g/10 min, or each less than or equal to 40 g/10 min.
 21. Thecomposite film according to claim 1, wherein the first component or thesecond component with a lower melting point in a cross-section of thebicomponent fiber forms an outer surface of the bicomponent fiber, andat least partially surrounds the component with a higher melting point.22. The composite film according to claim 1, wherein the polymer of oneof the first component or the second component has been polymerized witha metallocene catalyst.
 23. The composite film according to claim 22,wherein the polymer of the other of the first component or the secondcomponent has been polymerized with a Ziegler-Natta catalyst andsubjected to a subsequent visbreaking treatment.
 24. The composite filmaccording to claim 1, wherein the first component comprises an additive,a mass fraction of the additive in the second component being smallerthan in the first component, wherein the mass fraction is: at most66.6%, at most 50%, or at most 33.3%, of the mass fraction of theadditive in the first component.
 25. The composite film according toclaim 24, wherein the additive is a primary or secondary antioxidant, aUV absorber, a UV stabilizer, a flame retardant, an antistatic agent, alubricant, a metal deactivator, a hydrophilizing agent, a hydrophobizingagent, an anti-fogging additive and/or a biocide.
 26. The composite filmaccording to claim 24, wherein the additive is selected from the groupof: sterically hindered phenols, aromatic secondary or tertiary amines,aminophenols, aromatic nitro or nitroso compounds, organic phosphites orphosphonates, thioethers, thioalcohols, thioesters, sulfides andsulfur-containing organic acids, dithiocarbamates, thiodipropionates,aminopyrazoles, metal-containing chelates, mercaptobenzimidazoles,hydroxybenzophenones, cinnamates, oxalanilides, salicylates, resorcinolmonobenzoates, benzotriazoles, triazines, benzophenones, titaniumdioxide, carbon black, metal-containing complexes of organic sulfur orphosphorus compounds, sterically hindered amines (HALS), metalhydroxides, borates, organic bromine- or chlorine-containing compounds,organic phosphorus compounds, antimony trioxide, melamine, melaminecyanurate, exfoliated graphite or other intumescent systems, quaternaryammonium salts, alkyl sulfonates, alkyl sulfates, alkyl phosphates,dithiocarbamates, (alkaline earth) metal carboxylates, polyethyleneglycols and their esters and ethers, ethoxylates, mono- anddiglycerides, fatty alcohols, esters of fatty alcohols, fatty acids,fatty acid esters, dicarboxylic acid esters, fatty acid amides, metalsalts of fatty acids, polyolefin waxes, natural or artificial kerosenesand their derivatives, fluoropolymers and fluoroligomers, antiblockingagents, silicas, silicones, silicates, calcium carbonate, amides ofmono- and dicarboxylic acids and their derivatives, cyclic amides,hydrazones and bishydrazones, hydrazides, hydrazines, melamine and itsderivatives, benzotriazoles, aminotriazoles, sterically hindered phenolsin combination with complexing metal compounds, benzylphosphonates,pyridithiols, thiobisphenol esters, polyglycols, ethoxylates,fluoropolymers and fluoroligomers montan waxes, stearates,10,10′-oxybisphenoxarsine (OBPA), N-(trihalogen-methylthiol)phthalimide,tributyltin oxide, zinc dimethyldithiocarbamate,diphenylantimony-2-ethylhexanoate, copper-8-hydroxyquinoline,isothiazolones, silver and silver salts as biocides or mixtures thereof.27. The composite film according to claim 1, the first polymer and/orthe second polymer is: a polyolefin or a polyolefin copolymer, a polymerand/or copolymer of ethylene, propylene, butylene, hexene or octeneand/or a blend and/or a blend thereof, and/or a polyethyleneterephthalate and/or a polyethylene terephthalate copolymer.
 28. Thecomposite film according to claim 1, wherein a mass fraction of thefirst component or the second component with a lower melting point inthe bicomponent fiber is: at most 50%, at most 25%, at most 10%, or atmost 5%.
 29. An open-diffusion construction film comprising: at leastone functional layer; at least one outer protective layer; and at leastone inner protective layer, wherein: the at least one functional layeris positioned between the at least one outer protective layer and the atleast one inner protective layer, the film is open to diffusion, the atleast one functional layer includes thermoplastic polyurethane, the atleast one functional layer is at least a single-layer membrane layer,the at least one outer protective layer and the at least one innerprotective layer are formed as a nonwoven layer comprising polyolefin,one or more of the outer protective layer and/or the inner protectivelayer comprises at least one bicomponent fiber including a firstcomponent and a second component, wherein the first component comprisesa first polymer, and the second component comprises a second polymer.